3D Rapid Parts

High-Quality Prototype Service From Your Design Files

Rapid prototyping is ideal for fast design iterations and part testing. Our expertise and capabilities allow for a variety of material options and
ensure a consistently high level of quality while maintaining quick turnaround times. Our on-demand service will bring your prototypes to
life and create real functional end-use parts.

 

 

 

Enter your information below, and provide the details and any additional information regarding your project. Submit the STL, STP, SLDPRT or STEP files. Choose the desired materials below. You will receive a quote, and confirm your order.

 

Maximum upload size is 40meg. When sending multiple files, please place them in a zip file.

3D RapidParts

First Name Last Name
Company
EmailPhone
AddressCity
StateZip
Technology

    
Notes:
Upload File

The Send File & Data button will become active after all fields are filled in.

 

Best = •••••        Better = ••••        Good = •••


            

MarkForgedTough NylonOnyxCarbon CFFKevlar CFFFiberglass CFFHSHT Glass CFF
Tensile Modulus ASTM D638
0.94 (GPa)
1.4(GPa)
Tensile Stress at Yield ASTM D638
31 (MPa)
36 (MPa)
Tensile Strain at Yield ASTM D638
27%
25%
Tensile Stress at Break ASTM D638
54 (MPa)
30 (MPa)
Tensile Strain at Break ASTM D638
260%
58%
Tensile Strength ASTM D3039
700 (MPa)
610 (MPa)
590 (MPa)
600 (MPa)
Tensile Modulus ASTM D3039
54 (GPa)
27 (GPa)
21 (GPa)
21 (GPa)
Tensile Strain at Break ASTM D3039
1.5%
2.7%
3.8%
3.9%
Flexural Strength ASTM D790
32 (MPa)
81 (MPa)
470 (MPa)
190 (MPa)
210 (MPa)
420 (MPa)
Flexural Modulus ASTM D790
0.84 (GPa)
2.9 (GPa)
51 (GPa)
26 (GPa)
22 (GPa)
21 (GPa)
Flexural Strain at Break ASTM D790
n/a
n/a
1.2%
2.1%
1.1%
2.2%
Compression Strength ASTM D6441
320 (MPa)
97 (MPa)
140 (MPa)
192 (MPa)
Compression Modulus ASTM D6441
54 (GPa)
28 (GPa)
21 (GPa)
21 (GPa)
Compression Strain at Break ASTM D6441
0.7%
1.5%
n/a
n/a
Heat Deflection ASTM D648
49 °C
145 °C
105 °C
105 °C
105 °C
150 °C
Izod Impact — notched ASTM D256-10
1015 J/m
334 J/m
958 J/m
1873 J/m
2603 J/m
3117 J/m

            

MJPVisiJet M3 Hi-CastVisiJet M2R-WT
Color
Navy Blue
Opaque White
Density @ 20 °C (solid) ASTM D792
1.16 g/cm³
Density @ 80 °C (liquid) ASTM D3505
0.81 g/cm³
Tensile Strength ASTM D638
35-45 MPa
Tensile Modulus ASTM D638
1500-2000 MPa
Elongation at Break ASTM D638
20-30%
Flexural Strength ASTM D790
50-60 MPa
Flexural Modulus ASTM D790
1700-2200 MPa
Impact Strength (Notched Izod) ASTM D256
20-25 J/m
Shore D Hardness ASTM 2240
77
Water Absorption ASTM D570 24 hr
0.50%
Heat Distortion Temp @ 0.45 MPa ASTM D648
51 °C
Heat Distortion Temp @ 1.82 MPa ASTM D648
45 °C
Melting Point
70 °C
Softening Point
52-62 °C
Volumetric Shrinkage from 40 °C to RT
2.24%
Linear Shrinkage from 40 °C to RT
0.75%
Needle Penetration Hardness ASTM D1321
9
Ash Content ASTM 2584
<0.05%

            

SLA #1Accura 25Accura Xtreme 200Accura Xtreme GreyAccura 55Accura SL 7810Accura SL 7820
Class
Polyproplyene Like
Tough Durable
Tough Durable
ABS Like
ABS Like
ABS Like
Accuracy
••••
••••
••••
••••
•••
•••
HiTemp
Moisture Resistance
•••
•••
•••
••••
••••
Optical Clarity
Durability
••••
•••••
••••
•••
••••
••••
Color
White
White
Grey
White
White
Black
Investment Casting
Master Patterns
••••
•••
••••
•••
•••
•••
Snap Fit Assemblies
••••
•••••
••••
•••
•••
•••
General Purpose Models
••••
•••
••••
••••
•••
•••
Automotive
Wind Tunnel
Viscosity (cps) (@30°C)
250
650-750
250-300
155-185
210
210
Flexural Modulus (MPa) ASTM D 790
1380-1660
2350-2550
1520-2070
2690-3240
2040-2120
2260-2370
Flexural Strength (MPa) ASTM D 790
55-58
75-79
52-71
88-110
74-76
75-78
Tensile Modulus (MPa) ASTM D638
1590-1660
2300-2630
1790-1980
3200-3380
2290-2400
1890-2440
Tensile Strength (MPa) ASTM D 638
38
45-50
33-44
63-68
46-48
45-47
Elongation at Break ASTM D 638
13-20%
7-20%
14-22%
5-8%
8-14%
6-13%
Impact Strength (J/m) ASTM D 256
19-24
55-66
35-52
12-22
24-47
39-56
Heat Defl. Temp (°C) ASTM D 648 @66 PSI - 58-36
@264 PSI - 51-55
@66 PSI - 47
@264 PSI - 42
@66 PSI - 62
@264 PSI - 54
@66 PSI -55-58
@264 PSI - 51-53
@66 PSI - 51 @66 PSI - 51

          

SLA #2Accura ClearvueAccura 60Accura Cast ProAccura BluestoneAccura 48 HTRVisijet SL Clear
Class
Clear
Clear
Casting
High Temp
High Temp
Accuracy
•••
••••
••••
••••
HiTemp
••••
••••
Moisture Resistance
•••••
•••
•••••
••••
•••
Optical Clarity
•••••
•••
Durability
••••
•••
Color
Clear
Clear-bluish
Clear amber
Blue
Clear amber
Investment Casting
••••
•••••
Master Patterns
•••
••••
Snap Fit Assemblies
•••
••••
General Purpose Models
•••
•••••
Automotive
••••
Wind Tunnel
•••••
Viscosity (cps) (@30°C)
235-260
150-180
240-260
1200-1800
200-250
200-300
Flexural Modulus (MPa) ASTM D 790
1380-1660
2350-2550
1520-2070
2690-3240
2040-2120
2330
Flexural Strength (MPa) ASTM D 790
55-58
75-79
52-71
88-110
74-76
83
Tensile Modulus (MPa) ASTM D638
1590-1660
2300-2630
1790-1980
3200-3380
2290-2400
2560
Tensile Strength (MPa) ASTM D 638
38
45-50
33-44
63-68
46-48
52
Elongation at Break ASTM D 638
13-20%
7-20%
14-22%
5-8%
8-14%
6%
Impact Strength (J/m) ASTM D 256
19-24
55-66
35-52
12-22
24-47
46
Heat Defl. Temp (°C) ASTM D 648 @66 PSI - 58-36
@264 PSI - 51-55
@66 PSI - 47
@264 PSI - 42
@66 PSI - 62
@264 PSI - 54
@66 PSI -55-58
@264 PSI - 51-53
@66 PSI - 51
50° C

            

SLSDuraForm PADuraForm GFDuraForm EX WhiteDuraForm EX BlackDuraForm HST
Flexible/durable
••••
•••••
Non-rigid/durable tough
••••
••••
••••
High Temp resistance
•••
••••
•••
•••
••••
High elongation
•••
••••
••••
High-impact strength
••••
•••
•••••
•••••
••••
Accuracy
•••••
•••••
•••
•••
•••••
Surface finish
••••
•••
••••
••••
•••
Color
White
Pale grey
White
Black
Pale gray
Production parts
•••••
•••••
•••••
•••••
•••••
Parts w/snap fits
••••
•••••
•••••
Automotive design
•••••
••••
••••
••••
••••
Aerospace parts
••••
••••
•••••
•••••
•••••
Medical applications
•••••
Jigs/fixtures/tools
••••
•••••
•••
•••
•••••
Density sintered part ASTM 792
1.03 g/cm³
1.49 g/cm³
1.01 g/cm³
1.01 g/cm³
1.20 g/cm³
Flexural Modulus (MPa) ASTM D 790
1387
3106
1310
1310
4400-4550
Flexural Strength (MPa) ASTM D 790
48
37
46
46
83-89
Tensile Modulus (MPa) ASTM D638
1586
1517
1517
5475-5725
Tensile Strength (MPa) ASTM D 638
43
26
48
48
48-51
Elongation at Break ASTM D 638
14%
1.4%
47%
47%
4.5%
Impact Strength (J/m) ASTM D 256
Notched Izod, 23°C
Unnotched Izod, 23°C

32
336

41
123

74
1486

74
1486

37.4
310
Heat Defl. Temp (°C) ASTM D 648
@0.45MPa
@1.82 MPa

180° C
95° C

179° C
134° C

188° C
48° C

188° C
48° C

184° C
179° C
Flammability UL 94
HB
HB
HB
HB
HB
Hardness ASTM D2240
73D
75D
74D
74D
75D

            

DMPStainless 316LTitaniumAluminum Alloy ALSi12
Chemical Composition
Al
5.50-6.75%
Balance
C
≤0.030%
≤0.08%
Cr
16.5-18.5%
Fe
Balance
≤0.30%
H
≤0.0015%
Mn
≤2.00%
Mo
2.00-2.50%
N
≤0.11%
≤0.03%
Ni
10.00-13.00%
O
≤0.13%
P
≤0.045%
S
≤0.030%
Si
≤1.00%
11.0 - 13.0%
Ti
Balance
V
3.50-4.50%
Y
≤0.005%
Residuals each
≤0.10%
Residuals Total
≤0.40%
< 0.6%
Ultimate Tensile Strength ASTM E8
As-built
After post heat treatment

480 MPa ± 20
240 MPa ± 20
Yield Strength ASTM E8
As-built
After post heat treatment

270 MPa ± 20
180 MPa ± 20
Elongation at Break ASTM E8
As-built
After post heat treatment

5.5% ± 1.0
20% ± 4.0
Hardness
As-built
After post heat treatment

137 ± 1.5 HB
90 - 95 HB
Density
Approx. 100%
Young’s Modulus ASTM E8M
105 - 120 GPa
190 GPa
Yield Strength (Rp 0.2 %) ASTM E8M
950 MPa ± 30 MPa
1100 MPa ± 100 MP
330 MPa ±50 MPa
470 MPa ± 70 MP
Ultimate Tensile Strength ASTM E8M
1030 MPa ± 20 MPa
1190 MPa ± 100 MPa
550 MPa ± 50 MPa
600 MPa ± 100 MPa
Elongation at Break ASTM E8M
12% ± 2 %
8% ± 2%
50% ± 10%
40% ± 20%

          